TYPICAL PROPERTIES (1)
|
|
MECHANICAL/機(jī)械性能
|
Value/值
|
Unit/單位
|
Standard/標(biāo)準(zhǔn)
|
|
Tensile Stress, yld, Type I / 抗張程度,屈服,類(lèi)型I, 50 mm/min
|
62
|
MPa
|
ASTM D 638
|
|
Tensile Strain, brk, Type I / 拉伸伸長(zhǎng),斷裂,類(lèi)型I, 50 mm/min
|
40
|
%
|
ASTM D 638
|
|
Flexural Stress, yld / 撓曲強(qiáng)度, 屈服 , 2.6 mm/min, 100 mm span
|
102
|
MPa
|
ASTM D 790
|
|
Flexural Modulus / 撓曲模量, 2.6 mm/min, 100 mm span
|
2650
|
MPa
|
ASTM D 790
|
|
Hardness，Rockwell / 洛氏硬度 R
|
123
|
–
|
ASTM D 785
|
|
IMPACT/沖擊性能
|
Value/值
|
Unit/單位
|
Standard/標(biāo)準(zhǔn)
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強(qiáng)度, 23°C
|
534
|
J/m
|
ASTM D 256
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強(qiáng)度, -30°C
|
160
|
J/m
|
ASTM D 256
|
|
Instrumented IMPACT Total Energy / 裝有測(cè)量?jī)x表的落鏢沖擊總能量, 23°C
|
61
|
J
|
ASTM D 3763
|
|
Instrumented IMPACT Total Energy / 裝有測(cè)量?jī)x表的落鏢沖擊總能量, -30°C
|
54
|
J
|
ASTM D 3763
|
|
THERMAL/熱性能
|
Value/值
|
Unit/單位
|
Standard/標(biāo)準(zhǔn)
|
|
Vicat Softening Temp, Rate / 維卡軟化溫度，等級(jí) B/50
|
112
|
°C
|
ASTM D 1525
|
|
HDT（熱變形溫度）, 1.82 MPa, 3.2mm, unannealed （未退火）
|
90
|
°C
|
ASTM D 648
|
|
HDT（熱變形溫度）, 0.45 MPa, 6.4 mm, unannealed （未退火）
|
104
|
°C
|
ASTM D 648
|
|
HDT（熱變形溫度）, 1.82 MPa, 6.4 mm, unannealed （未退火）
|
95
|
°C
|
ASTM D 648
|
|
CTE（線形膨脹系數(shù)）, -30°C to 30°C, flow（流動(dòng)）
|
7.2E-05
|
1/°C
|
ASTM D 696
|
|
CTE（線形膨脹系數(shù)）, -30°C to 30°C, xflow（橫向）
|
7.2E-05
|
1/°C
|
ASTM D 696
|
|
Thermal Conductivity / 導(dǎo)熱系數(shù)
|
0.2
|
W/m-°C
|
ASTM C 177
|
|
Relative Temp Index, Elec / 相對(duì)熱指數(shù)， 電性能
|
85
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact / 相對(duì)熱指數(shù)，機(jī)械沖擊性能
|
85
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact / 相對(duì)熱指數(shù)，非機(jī)械沖擊性能
|
85
|
°C
|
UL 746B
|
|
PHYSICAL/物理性能
|
Value/值
|
Unit/單位
|
Standard/標(biāo)準(zhǔn)
|
|
Specific Gravity / 比重
|
1.18
|
–
|
ASTM D 792
|
|
Specific Gravity / 比重, color
|
1.22
|
–
|
ASTM D 792
|
|
Water Absorption / 吸水率, 24 hours
|
0.1
|
%
|
ASTM D 570
|
|
Water Absorption，equilibrium / 吸水率，平衡, 23C
|
0.4
|
%
|
ASTM D 570
|
|
Mold Shrinkage / 收縮率, flow（流動(dòng)）, 3.2 mm
|
0.4 – 0.6
|
%
|
SABIC Method
|
|
Mold Shrinkage / 收縮率, xflow（橫向）, 3.2 mm
|
0.4 – 0.6
|
%
|
SABIC Method
|
|
Melt Flow Rate / 熔流率,, 260°C/2.16 kgf
|
10
|
g/10 min
|
ASTM D 1238
|
|
ELECTRICAL/電氣性能
|
Value/值
|
Unit/單位
|
Standard/標(biāo)準(zhǔn)
|
|
Volume Resistivity / 體積電阻率
|
1.E+17
|
Ohm-cm
|
ASTM D 257
|
|
Surface Resistivity / 表面電阻率
|
>1.E+16
|
Ohm
|
ASTM D 257
|
|
Dielectric Strength, in oil / 耐電強(qiáng)度，在油中, 3.2 mm
|
19.4
|
kV/mm
|
ASTM D 149
|
|
Relative Permittivity / 相對(duì)介電常數(shù), 50/60 Hz
|
3
|
–
|
ASTM D 150
|
|
Relative Permittivity / 相對(duì)介電常數(shù), 100 Hz
|
3
|
–
|
ASTM D 150
|
|
Dissipation Factor / 耗散因素, 50/60 Hz
|
0.005
|
–
|
ASTM D 150
|
|
Dissipation Factor / 耗散因素, 100 Hz
|
0.0049
|
–
|
ASTM D 150
|
|
Arc Resistance, Tungsten / 耐電弧性 {PLC}
|
6
|
PLC Code
|
ASTM D 495
|
|
Hot Wire Ignition / 熱絲引燃 {PLC)
|
1
|
PLC Code
|
UL 746A
|
|
High Voltage Arc Track Rate / 高電壓電弧起痕速率 {PLC}
|
2
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface / 高電流電弧引燃，表面 {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index / 相比耐漏電起痕指數(shù) (UL) {PLC}
|
1
|
PLC Code
|
UL 746A
|
|
FLAME CHARACTERISTICS/火焰特性
|
Value/值
|
Unit/單位
|
Standard/標(biāo)準(zhǔn)
|
|
UL Recognized, 94V-0 Flame Class Rating / 阻燃等級(jí) (3)
|
1.49
|
mm
|
UL 94
|
|
UL Recognized, 94-5VB Rating (3)
|
2.48
|
mm
|
UL 94
|
|
CSA (See File for complete listing)
|
LS88480
|
File No.
|
CSA LISTED
|
|
Oxygen Index / 極限氧指數(shù) (LOI)
|
32
|
%
|
ASTM D 2863
|
點(diǎn)擊圖片查看大圖
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買(mǎi)/賣(mài)家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。